Wet oxidation of amorphous Si0.67Ge0.25C 0.08 grown on (100) Si substrates

A. E. Bair, Z. Atzmon, Terry Alford, David Smith

Research output: Contribution to journalArticlepeer-review

5 Scopus citations


Wet oxidation annealing of thin films of amorphous Si0.67Ge 0.25C0.08 was performed over the temperature range from 700 to 950 °C. Changes in composition and microstructure were assessed using Rutherford backscattering spectrometry and transmission electron microscopy. A nearly pure layer of SiO2 with approximately 1 at. % carbon was formed, with Ge being rejected from the oxide at all temperatures. At low temperatures, the oxide formed was very thin. Ge piled up at the oxide/film interface and the thin film microstructure remained amorphous. At higher temperatures, a network of nanocrystals was observed which was believed to provide a grain boundary diffusion path for Ge which had redistributed throughout the remaining layer. It is proposed that the Ge layer had inhibited oxidation at the lower temperatures, whereas its removal resulted in increased oxidation rates at higher temperatures. Annealing at 950 °C for 5 and 6 h resulted in an epitaxial transformation and a single crystal structure. This process occurred as a result of the silicon being removed from the substrate by the oxide front which served as a sink. Germanium then diffused into the vacancies in the substrate forming a new epitaxial layer.

Original languageEnglish (US)
Pages (from-to)2835-2841
Number of pages7
JournalJournal of Applied Physics
Issue number5
StatePublished - 1998

ASJC Scopus subject areas

  • Physics and Astronomy(all)


Dive into the research topics of 'Wet oxidation of amorphous Si0.67Ge0.25C 0.08 grown on (100) Si substrates'. Together they form a unique fingerprint.

Cite this