Kinetics of Ag/Al bilayer self-encapsulation

Y. Wang, Terry Alford, J. W. Mayer

Research output: Contribution to journalArticlepeer-review

17 Scopus citations


The self-encapsulation kinetics of Ag/Al bilayers were studied both experimentally and theoretically as part of the effort to introduce Ag as an alternative metallization scheme for future ultra-large-scale-integrated technologies. Theoretical modeling was based on an analytical solution of a modified diffusion equation, which incorporated the diffusion of Al atoms through the Ag layers during the Ag/Al bilayer encapsulation progress. The amount of segregated Al atoms was monitored by both Rutherford backscattering spectrometry and film resistivity measurements, and correlated well with the theoretical predictions. These findings showed that the kinetics of the self-encapsulation could be significantly affected by both (i) the chemical affinity between Al and Ag atoms, and (ii) the interfacial energy between the metal layer (Ag) and the newly formed AlxOyNz diffusion barriers. Higher anneal temperatures were shown to accelerate the encapsulation process, and hence, achieved a lower resistivity in the underneath Ag layer. This model, in addition, confirmed the self-passivating characteristics of AlxOyNz diffusion barriers formed by Ag/Al bilayers annealed between 500 and 725°C.

Original languageEnglish (US)
Pages (from-to)5407-5412
Number of pages6
JournalJournal of Applied Physics
Issue number10
StatePublished - Nov 15 1999

ASJC Scopus subject areas

  • Physics and Astronomy(all)


Dive into the research topics of 'Kinetics of Ag/Al bilayer self-encapsulation'. Together they form a unique fingerprint.

Cite this